Analysis of the sealing system of a high performance pneumatic hammer

Objective

To reproduce the wear mechanisms of the sealing system of a high speed pneumatic hammer under different operating conditions.

Results

Fatigue, extrusion and thermal degradation were identified as the main failure mechanisms.

Analysis of the sealing system of a high performance pneumatic hammer

Seals are critical elements of a variety of industrial products. The aim of this study was to reproduce the wear mechanisms for the sealing systems of pneumatic hammers to know how to respond to each type of seal and material under actual working conditions.

To address this study, a specific test chamber was designed to test piston seals at a linear velocity of 6 m/s and pressurised with compressed air. During the wear testing, the pressure in the chamber and the temperature in the sleeve were monitored with the aim of measuring possible leaks and frictional heating, respectively, during the test. Fatigue, extrusion and thermal degradation were the main failure mechanisms identified.

Fields of application:

Energy, Capital goods, Machine Tools, Transport.

This site uses cookies

We use cookies to improve the browsing experience and provide our services to you.

If you continue browsing, we consider that you accept their use.

If you wish to obtain additional information, please query our Cookies policy.

Accept